Translucent RTV R-1310 A/B
R-1310 A/B Tin-Based, Translucent Silicone RTV rubber intended primarily for making puppet skins and highly flexible rubber parts. It is also used as a general purpose, high strength rubber.
Features:
*Excellent Physical Properties with High Tear Resistance
*Low Viscosity
*Flesh Skin Softness
*Fast Cure (3hour) Brush-On Catalyst R-1300TH SP B
|
|
R-1310 A/B |
R-1300TH SP B Catalyst
|
Softner F-100 |
|
Color: |
Translucent |
Clear |
Clear |
|
Mix Ratio A to B: |
Pourable 100/10 |
Brush-On 100/10 |
10 to 200% |
|
Mixed Viscosity: |
18,000 |
Thixotropic |
50 |
|
Specific Gravity: |
1.08 |
1.08 |
1 |
|
Hardness A Shore: |
10 |
6 |
Varies |
|
Tensile Strength PSI: |
375 |
* Gel 30 min |
NA |
|
Elongation: |
500 |
* Cure 3 hours |
NA |
|
Tear Resistance: |
70 |
NA |
NA |
|
|
|
|
|
Mixing Instructions:
R-1310 A/B is processed by adding the curing agent B. The addition of 10% catalyst (by weight) has a pot life of 45 minutes – 1 hour. Since material is clear, a double mix is recommended to ensure a thorough mix. Softening agent F-100 can be used to create a gel like silicone medium for movement or additional soft feeling. After the mold (or part) has been removed from the master, it should be left for 24 hours in order to develop its maximum mechanical strength.
The information and data contained herein are based on information we believe reliable. Each user of the material should thoroughly test any application and independently conclude satisfactory performance before commercializing. Suggestions of uses should not be taken as inducements to infringe on any particular patent.